The FFC Cambridge Process is an electrochemical method in which solid metal compounds, particularly oxide
s, are cathodically reduced to the respective metals or alloy
s in molten salts. It is thought that this process will eventually be capable of producing metals or alloys more efficiently than current conventional processes, e.g. Ti using the Kroll process
.
. (The name FFC derives from the first letters of their last names.) They reduced oxide scales on titanium foils, as well as small pellets of titanium dioxide
powder, to the metal by molten salt electrochemistry. The technology has since been commercialised in the form of an intellectual property company known as Metalysis, which is based in Sheffield, UK. A similar process was patented in 1904 as German patent 150557.
When negative voltages are reached, it is possible that the cathode would begin to produce Ca (which is soluble in CaCl2). Ca is highly reductive and would further strip oxygen from the cathode, resulting in calciothermic reduction. However, Ca dissolved into CaCl2 results in a more conductive salt leading to reduced current efficiencies.
(1)
When this reaction takes place on its own, it is referred to as the "calciothermic
reduction" (or, more generally, an example of metallothermic reduction). For example, if the cathode was primarily made from TiO then calciothermic reduction would appear as:
Whilst the cathode reaction can be written as above it is in fact a gradual removal of oxygen from the oxide. For example, it has been shown that TiO2 does not simply reduce to Ti. It, in fact, reduces through the lower oxides (Ti3O5, Ti2O3, TiO etc.) to Ti.
The calcium oxide produced is then electrolyzed:
(2a)
(2b)
and
(2c)
Reaction (2b) describes the production of Ca metal from Ca2+ ions within the salt, at the cathode. The Ca would then proceed to reduce the cathode.
The net result of reactions (1) and (2) is simply the reduction of the oxide into metal plus oxygen:
(3)
(d)
(e)
However, if an inert anode is used, such as that of high density SnO2, the discharge of the O2– ions leads to the evolution of oxygen gas. However the use of an inert anode has disadvantages. Firstly, when the concentration of CaO is low, Cl2 evolution at the anode becomes more favourable. In addition, when compared to a carbon anode, more energy is required to achieve the same reduced phase at the cathode. Inert anodes suffer from stability issues.
(f) Inert anode: 2 O2– → O2 (g) + 4 e
Oxide
An oxide is a chemical compound that contains at least one oxygen atom in its chemical formula. Metal oxides typically contain an anion of oxygen in the oxidation state of −2....
s, are cathodically reduced to the respective metals or alloy
Alloy
An alloy is a mixture or metallic solid solution composed of two or more elements. Complete solid solution alloys give single solid phase microstructure, while partial solutions give two or more phases that may or may not be homogeneous in distribution, depending on thermal history...
s in molten salts. It is thought that this process will eventually be capable of producing metals or alloys more efficiently than current conventional processes, e.g. Ti using the Kroll process
Kroll process
Kroll Process is a pyrometallurgical industrial process used to produce metallic titanium. It was invented by William J. Kroll in Luxembourg. After moving to the United States, Kroll further developed the method for the production of zirconium...
.
History
The FFC Cambridge process was developed by George Z. Chen, Derek J. Fray and Tom W. Farthing between 1996 and 1997 in the University of CambridgeUniversity of Cambridge
The University of Cambridge is a public research university located in Cambridge, United Kingdom. It is the second-oldest university in both the United Kingdom and the English-speaking world , and the seventh-oldest globally...
. (The name FFC derives from the first letters of their last names.) They reduced oxide scales on titanium foils, as well as small pellets of titanium dioxide
Titanium dioxide
Titanium dioxide, also known as titanium oxide or titania, is the naturally occurring oxide of titanium, chemical formula . When used as a pigment, it is called titanium white, Pigment White 6, or CI 77891. Generally it comes in two different forms, rutile and anatase. It has a wide range of...
powder, to the metal by molten salt electrochemistry. The technology has since been commercialised in the form of an intellectual property company known as Metalysis, which is based in Sheffield, UK. A similar process was patented in 1904 as German patent 150557.
Process
The process typically takes place between 900–1100 °C, with an anode (typically carbon) and a cathode (oxide being reduced) in a bath of molten CaCl2. Depending on the nature of the oxide it will exist at a particular potential relative to the anode, which is dependent on the quantity of CaO present in CaCl2. The cathode is then polarised to a more negative voltages versus the anode. This is simply achieved by imposing a voltage between the anode and cathode. When polarised to more negative voltages the oxide releases oxygen ions into the CaCl2 salt, which exists as CaO. To maintain charge neutrality; as oxygen ions are released from the cathode into the salt, so oxygen ions must be released from the salt to the anode. This is observed as CO or CO2 being evolved at the carbon anode. In theory an inert anode could be used to produce oxygen.When negative voltages are reached, it is possible that the cathode would begin to produce Ca (which is soluble in CaCl2). Ca is highly reductive and would further strip oxygen from the cathode, resulting in calciothermic reduction. However, Ca dissolved into CaCl2 results in a more conductive salt leading to reduced current efficiencies.
Cathode reaction mechanism
The electro-calciothermic reduction mechanism may be represented by the following sequence of reactions.(1)
When this reaction takes place on its own, it is referred to as the "calciothermic
Calciothermic reaction
Calciothermic reactions are metallothermic reduction reactions which use calcium metal as the reducing agent at high temperature....
reduction" (or, more generally, an example of metallothermic reduction). For example, if the cathode was primarily made from TiO then calciothermic reduction would appear as:
Whilst the cathode reaction can be written as above it is in fact a gradual removal of oxygen from the oxide. For example, it has been shown that TiO2 does not simply reduce to Ti. It, in fact, reduces through the lower oxides (Ti3O5, Ti2O3, TiO etc.) to Ti.
The calcium oxide produced is then electrolyzed:
(2a)
(2b)
and
(2c)
Reaction (2b) describes the production of Ca metal from Ca2+ ions within the salt, at the cathode. The Ca would then proceed to reduce the cathode.
The net result of reactions (1) and (2) is simply the reduction of the oxide into metal plus oxygen:
(3)
Anode reaction mechanism
The use of molten CaCl2 is important because this molten salt can dissolve and transport the O2– ions to the anode to be discharged. The anode reaction depends on the material of the anode. Depending on the system it is possible to produce either CO or CO2 or a mixture at the carbon anode.(d)
(e)
However, if an inert anode is used, such as that of high density SnO2, the discharge of the O2– ions leads to the evolution of oxygen gas. However the use of an inert anode has disadvantages. Firstly, when the concentration of CaO is low, Cl2 evolution at the anode becomes more favourable. In addition, when compared to a carbon anode, more energy is required to achieve the same reduced phase at the cathode. Inert anodes suffer from stability issues.
(f) Inert anode: 2 O2– → O2 (g) + 4 e