Built-up gun
Encyclopedia
The term built-up gun describes a construction technique for artillery barrels. An inner tube of metal which stretches most within its elastic limit enlarges under the pressure of confined powder gases to transmit stress to outer cylinders under tension. Concentric metal cylinders and/or wire windings are assembled to minimize the weight required to resist the pressure of powder gases pushing a projectile out of the barrel. Built-up construction was the norm for guns mounted aboard 20th century Dreadnought
s and contemporary railway gun
s, coastal artillery
, and siege guns through World War II
.
or smokeless powder
gasses pushing the shell out of a gun barrel; but a gun will be deformed or explode if chamber pressures strain
a gun barrel beyond the elastic limit of the metal from which the barrel is made. Thickness of homogeneous cast metal gun barrels reached a useful limit at approximately one-half caliber. Additional thickness provided little practical benefit, since higher pressures generated cracks from the bore before the outer portion of the cylinder could respond, and those cracks would extend outward during subsequent firings.
Claverino's 1876 treatise on the "Resistance of Hollow Cylinders" was published in Giornale d'Artigliera. The concept was to give exterior portions of the gun initial tension, gradually decreasing toward the interior, while giving interior parts a normal state of compression by the outer cylinders and wire windings. Theoretical maximum performance would be achieved if the inner cylinder forming the rifled bore were compressed to its elastic limit by surrounding elements while at rest before firing, and expanded to its elastic limit by internal gas pressure during firing.
. The jacket usually extends forward through the areas of highest pressure, through the recoil slide, and may extend all the way to the muzzle. The forward part of the barrel may be tapered toward the muzzle because less strength is required for reduced pressures as the projectile nears the muzzle. This tapered portion of barrel is called the chase. Very large guns sometimes use shorter outer cylinders called hoops when manufacturing limitations make full length jackets impractical. Hoops forward of the slide are called chase hoops. The jacket or forward chase hoop may be flared outward in the form of a bell at the muzzle for extra strength to reduce splitting because the metal at that point is not supported on the forward end. As many as four or five layers, or hoop courses, of successively tensioned cylinders have been used. Layers are designated alphabetically as the "A" tube enclosed by the "B" jacket and chase hoops, enclosed by the "C" hoop course, enclosed by the "D" hoop course, etc. Individual hoops within a course are numbered from the breech forward as the B1 jacket, the B2 chase hoop, and then the C1 jacket hoop, the C2 hoop etc. Successive hoop course joints are typically staggered and individual hoop courses use lap joints in preference to butt joints to minimize the weakness of joint locations. Cylinder diameter may be varied by including machined shoulders to prevent forward longitudinal movement of an inner cylinder within an outer cylinder during firing. Shoulder locations are similarly staggered to minimize weakness.
, a bored monoblock tube is filled with hydraulic fluid at pressures higher than the finished gun will experience during firing. Upon release of hydraulic pressure, the internal diameter of the monoblock tube will have been increased by approximately six percent; but the outer portion of the finished monoblock rebounds to approximate its original diameter and exerts compressive forces on the inner portion similar to the separate cylinders of a built-up gun.
Dreadnought
The dreadnought was the predominant type of 20th-century battleship. The first of the kind, the Royal Navy's had such an impact when launched in 1906 that similar battleships built after her were referred to as "dreadnoughts", and earlier battleships became known as pre-dreadnoughts...
s and contemporary railway gun
Railway gun
A railway gun, also called a railroad gun, is a large artillery piece, often surplus naval ordnance, mounted on, transported by, and fired from a specially designed railway wagon. Many countries have built railway guns, but the best known are the large Krupp-built pieces used by Germany in World...
s, coastal artillery
Coastal artillery
Coastal artillery is the branch of armed forces concerned with operating anti-ship artillery or fixed gun batteries in coastal fortifications....
, and siege guns through World War II
World War II
World War II, or the Second World War , was a global conflict lasting from 1939 to 1945, involving most of the world's nations—including all of the great powers—eventually forming two opposing military alliances: the Allies and the Axis...
.
Background
Velocity and range of artillery vary directly with pressure of gunpowderGunpowder
Gunpowder, also known since in the late 19th century as black powder, was the first chemical explosive and the only one known until the mid 1800s. It is a mixture of sulfur, charcoal, and potassium nitrate - with the sulfur and charcoal acting as fuels, while the saltpeter works as an oxidizer...
or smokeless powder
Smokeless powder
Smokeless powder is the name given to a number of propellants used in firearms and artillery which produce negligible smoke when fired, unlike the older gunpowder which they replaced...
gasses pushing the shell out of a gun barrel; but a gun will be deformed or explode if chamber pressures strain
Deformation (mechanics)
Deformation in continuum mechanics is the transformation of a body from a reference configuration to a current configuration. A configuration is a set containing the positions of all particles of the body...
a gun barrel beyond the elastic limit of the metal from which the barrel is made. Thickness of homogeneous cast metal gun barrels reached a useful limit at approximately one-half caliber. Additional thickness provided little practical benefit, since higher pressures generated cracks from the bore before the outer portion of the cylinder could respond, and those cracks would extend outward during subsequent firings.
Claverino's 1876 treatise on the "Resistance of Hollow Cylinders" was published in Giornale d'Artigliera. The concept was to give exterior portions of the gun initial tension, gradually decreasing toward the interior, while giving interior parts a normal state of compression by the outer cylinders and wire windings. Theoretical maximum performance would be achieved if the inner cylinder forming the rifled bore were compressed to its elastic limit by surrounding elements while at rest before firing, and expanded to its elastic limit by internal gas pressure during firing.
Nomenclature
The innermost cylinder forming the chamber and rifled bore is called a tube or, with certain construction techniques, a liner. A second layer cylinder called the jacket extends rearward past the chamber to house the breechblockBreechblock
A breechblock is the part of the firearm action that closes the breech of a weapon at the moment of firing....
. The jacket usually extends forward through the areas of highest pressure, through the recoil slide, and may extend all the way to the muzzle. The forward part of the barrel may be tapered toward the muzzle because less strength is required for reduced pressures as the projectile nears the muzzle. This tapered portion of barrel is called the chase. Very large guns sometimes use shorter outer cylinders called hoops when manufacturing limitations make full length jackets impractical. Hoops forward of the slide are called chase hoops. The jacket or forward chase hoop may be flared outward in the form of a bell at the muzzle for extra strength to reduce splitting because the metal at that point is not supported on the forward end. As many as four or five layers, or hoop courses, of successively tensioned cylinders have been used. Layers are designated alphabetically as the "A" tube enclosed by the "B" jacket and chase hoops, enclosed by the "C" hoop course, enclosed by the "D" hoop course, etc. Individual hoops within a course are numbered from the breech forward as the B1 jacket, the B2 chase hoop, and then the C1 jacket hoop, the C2 hoop etc. Successive hoop course joints are typically staggered and individual hoop courses use lap joints in preference to butt joints to minimize the weakness of joint locations. Cylinder diameter may be varied by including machined shoulders to prevent forward longitudinal movement of an inner cylinder within an outer cylinder during firing. Shoulder locations are similarly staggered to minimize weakness.
Assembly Procedure
After the tube, jacket, and hoops have been machined to appropriate dimensions, the jacket is carefully heated to approximately 400 degrees Celsius (800 degrees Fahrenheit) in a vertical air furnace so thermal expansion allows the cool tube to be lowered into place. When the jacket is in position, it is cooled to form a tensioned shrink fit over the tube. Then the next hoop (either B2 or C1) is similarly heated so the assembled A tube and B1 jacket can be lowered into position for a successive shrink fit. The assembled unit may be machined prior to fitting a new hoop. The process continues as remaining tubes are heated sequentially and cooled onto the built-up unit until all elements have been assembled. When tensioned wire winding is used in place of a hoop course, the wire is typically covered by an outer tensioned cylinder also called a jacket.Liners
Burning powder gasses melt part of the bore each time a gun is fired. This melted metal is oxidized or blown out of the muzzle until the barrel is eroded to the extent shell dispersion becomes unacceptable. After firing several hundred shells, a gun may be reconditioned by boring out the interior and inserting a new liner as the interior cylinder. Exterior cylinders are heated as a unit to approximately 200 degrees Celsius (400 degrees Fahrenheit) to allow insertion of a new liner and the liner is bored and rifled after installation. A new liner may be bored for a different projectile diameter than used in the original gun. Liners may be either cylindrical or conical. Conical liners are tapered toward the muzzle for ease of removal from the breech end while limiting forward creep during firing. Conical liners may be removed by water cooling the liner after re-heating the barrel, but cylindrical liners must be bored out.Monoblock Guns
With the obsolescence of very large guns following World War II, metallurgical advances encouraged use of monoblock (one-piece) construction for postwar guns of medium caliber. In a procedure called autofrettageAutofrettage
Autofrettage is a metal fabrication technique in which a pressure vessel is subjected to enormous pressure, causing internal portions of the part to yield and resulting in internal compressive residual stresses. The goal of autofrettage is to increase the durability of the final product...
, a bored monoblock tube is filled with hydraulic fluid at pressures higher than the finished gun will experience during firing. Upon release of hydraulic pressure, the internal diameter of the monoblock tube will have been increased by approximately six percent; but the outer portion of the finished monoblock rebounds to approximate its original diameter and exerts compressive forces on the inner portion similar to the separate cylinders of a built-up gun.